P265GH簡(jiǎn)介

牌號(hào) P265GH
歐標(biāo)鋼號(hào) 1.0425
對(duì)應(yīng)標(biāo)準(zhǔn) EN 10222-2-2017
壓力用途用鋼制鍛件 第2部分 具有高溫特性的鐵素體和馬氏體鋼
Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
歸類 碳鋼
P265GH 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Cu Mo Ti V Nb 更多
最小值 - - 0.5 - - - - - - - - - Cr+Cu+Mo+Ni≤0.70
最大值 0.2 0.4 1.4 0.03 0.025 0.3 0.3 0.3 0.08 0.03 0.02 0.01
碳當(dāng)量計(jì)算
P265GH 機(jī)械性能
厚度
t
mm		 熱處理或狀態(tài)
抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
% 		沖擊吸收能量
KV2
J
t≤60 奧氏體化或固溶退火,890~950℃,空冷 410~530 ≥245 I：≥29，tr/t：≥27 I：≥40，tr/t：≥27
60＜t≤100 奧氏體化或固溶退火,890~950℃,空冷 410~530 ≥215 I：≥26，tr/t：≥24 I：≥40，tr/t：≥27
① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.
1 近似對(duì)照表 鍋爐和壓力容器用鋼板
中國(guó) 日本 美國(guó) 國(guó)際標(biāo)準(zhǔn)組織 歐標(biāo) 俄羅斯
GB JIS ASTM ISO EN 數(shù)字牌號(hào) GOST
Q245R SEV245 Gr.65(450) P265GH P265GH 1.0425 16ГС
2 近似對(duì)照表 碳素結(jié)構(gòu)鋼和工程用鋼
日本 美國(guó) 國(guó)際標(biāo)準(zhǔn)組織 德國(guó) 法國(guó) 歐標(biāo) 俄羅斯 瑞典 英國(guó)
JIS ASTM ISO W-Nr. NF EN/NF EN 數(shù)字牌號(hào) GOST SS BS EN/BS
SG295 A414E
A516Gr.60
Gr.A 		F5
F7 		1.0425 A42AP
A42CP
A42F 		P265GH 1.0425 16K
20K 		1430
1431 		151-400
161-430
161Gr.400
164Gr.400
244Gr.400